Polystone® MK FL + AST black

PE — PE-UHMW - PE 1000

black, similar RAL 9005
profilerodsheet
QR-Code

Characteristics

  • Certified according to EN 45545-2
  • Self-extinguishing
  • Antistatic

Variants

Technical Specifications Polystone® MK FL + AST black extruded

Test MethodUnitGuideline Value
DensityDIN EN ISO 1183-1g / cm3>1,0
Water absorptionDIN EN ISO 62%0,1
Flammability (Thickness 3 mm / 6 mm)UL 94V0
Molecular weight-106 g/mol 9
Test MethodUnitGuideline Value
Yield stressDIN EN ISO 527MPa>20
Tensile modulus of elasticityDIN EN ISO 527MPa>1000
Shore hardnessDIN EN ISO 868scale D>63
Test MethodUnitGuideline Value
Melting temperatureISO 11357-3°C130 ... 135
Coefficient of linear thermal expansionDIN 5375210-6 / K150 ... 230
Service temperature, long termAverage°C-200 … 80
Service temperature, short term (max.)Average°C130
Vicat softening temperatureDIN EN ISO 306, Vicat B°C79
Test MethodUnitGuideline Value
Volume resistivityDIN EN 62631-3-1Ω * cm109
Surface resistivityDIN EN 62631-3-2Ω109

Technical Specifications Polystone® MK FL + AST black pressed

Test MethodUnitGuideline Value
DensityDIN EN ISO 1183-1g / cm3>1,0
Water absorptionDIN EN ISO 62%0,1
Flammability (Thickness 3 mm / 6 mm)UL 94V0
Molecular weight-106 g/mol 9
Test MethodUnitGuideline Value
Yield stressDIN EN ISO 527MPa>20
Tensile modulus of elasticityDIN EN ISO 527MPa>1000
Shore hardnessDIN EN ISO 868scale D>63
Test MethodUnitGuideline Value
Melting temperatureISO 11357-3°C130 ... 135
Coefficient of linear thermal expansionDIN 5375210-6 / K150 ... 230
Service temperature, long termAverage°C-200 … 80
Service temperature, short term (max.)Average°C130
Vicat softening temperatureDIN EN ISO 306, Vicat B°C79
Test MethodUnitGuideline Value
Volume resistivityDIN EN 62631-3-1Ω * cm109
Surface resistivityDIN EN 62631-3-2Ω109

Contact

您可以选择在信息中附加文件。文件必须是JPEG、PNG、BMP、PDF格式。请确保添加的文件不超过8 MB

Information on data protection can be found here.

更新
 
Search
联系方式

Share

新闻通讯注册

Select Website

Roechling_Industrial_Banner.jpg
用于技术领域的塑料

Industrial