Sustamid® 6G LU red
PA — PA 6 G
The sliding optimized material
Sustamid® 6 GLU is a shape-polymerized polyamide 6, modified with an incorporated lubricant. This ensures a permanently high lubricating effect, which is maintained even with increasing friction temperatures. The standard color of the material is red. Ideal for applications with increased sliding and wear loads.
coral red, similar RAL 3016
sheetrod
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 102185 | Sustamid® 6G LU red in-mould polymerised | sheet | sheet | coral red, similar RAL 3016 | 10 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 10 mm | ||
| No stock item (MOQ) | 643895 | Sustamid® 6G LU red in-mould polymerised | sheet | sheet | coral red, similar RAL 3016 | 27x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 27 mm | ||
| No stock item (MOQ) | 920525 | Sustamid® 6G LU red in-mould polymerised | rod | rod | coral red, similar RAL 3016 | Ø 76 x 3050 mm | 3,050 mm | 76 mm | |||
| No stock item (MOQ) | 920531 | Sustamid® 6G LU red in-mould polymerised | sheet | sheet | coral red, similar RAL 3016 | 27 x 1250 x 2500 mm | 2,500 mm | 1,250 mm | 27 mm |
Technical Specifications Sustamid® 6G LU red
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,14 |
| Water absorption | DIN EN ISO 62 | % | 2,0 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 70 |
| Elongation at break | DIN EN ISO 527 | % | 30 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3400 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 82 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 214 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,25 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -40 … 110 |
| Service temperature, short term (max.) | Average | °C | 160 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 90 |