Sustamid® 6G OL red
PA — PA 6 G
The PA 6 G material for a smooth run
Sustamid® 6 GOL is a cast-polymerized polyamide 6 that ensures optimized sliding properties thanks to the homogeneous distribution of a liquid lubricant in the finest form in the polymer. Compared to the modified Sustamid® 6 G, the integrated liquid lubricant significantly reduces friction and effectively prevents jerky sliding (“stick-slip effect”), enabling smooth movement.
brown red, similar RAL 3011
sheet
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 628710 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 11 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 11 mm | ||
| No stock item (MOQ) | 628713 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 100 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 100 mm | ||
| No stock item (MOQ) | 631557 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 20 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 20 mm | ||
| No stock item (MOQ) | 646896 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 98 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 98 mm | ||
| No stock item (MOQ) | 701264 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 60 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 60 mm | ||
| No stock item (MOQ) | 710851 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 98 x 1250 x 2500 mm | 2,500 mm | 1,250 mm | 98 mm | ||
| No stock item (MOQ) | 737343 | Sustamid® 6G OL red in-mould polymerised | sheet | sheet | brown red, similar RAL 3011 | 105 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 105 mm |
Technical Specifications Sustamid® 6G OL red
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,14 |
| Water absorption | DIN EN ISO 62 | % | 2,0 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 70 |
| Elongation at break | DIN EN ISO 527 | % | 50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3300 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 82 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 213 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,25 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -40 … 110 |
| Service temperature, short term (max.) | Average | °C | 160 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 90 |