Polystone® G HG white
PE — PE-HD - PE 300
High-performance polyethylene especially for the Healthcare industry
Due to its excellent chemical resistance, hygienic surface and high stability, it offers a wide range of possible applications in the healthcare sector – especially to produce complex components. From pharmaceutical production and analytical processes to innovative transport solutions - this material can make a significant contribution to optimising processes, cost-effectiveness and increasing product safety.
white, similar RAL 9010
sheet
Characteristics
- Good machinability
- Good mechanical properties
- ISO 10993-5 tested on semi-finished product
- Good weldability
- Chemical resistant
Industries
We are a system supplier and partner from the idea to the OEM's end product - as a cooperative value contribution. We are able to support the healthcare industry at the highest level.
Industry Manager Healthcare - Mail: AReuner@roechling.com
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 504509 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 15 mm | 3,000 mm | 1,500 mm | 15 mm | ||
| No stock item (MOQ) | 504510 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 20 mm | 3,000 mm | 1,500 mm | 20 mm | ||
| No stock item (MOQ) | 504513 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 10 mm | 3,000 mm | 1,500 mm | 10 mm | ||
| No stock item (MOQ) | 504514 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 2.000 x 15 mm | 3,000 mm | 2,000 mm | 15 mm | ||
| No stock item (MOQ) | 505286 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 30 mm | 3,000 mm | 1,500 mm | 30 mm | ||
| No stock item (MOQ) | 505287 | Polystone® G HG white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 6 mm | 3,000 mm | 1,500 mm | 6 mm | ||
| No stock item (MOQ) | 507378 | Polystone® G HG white pressed | sheet | sheet | white, similar RAL 9010 | 2.000 x 1.000 x 60 mm | 2,000 mm | 1,000 mm | 60 mm |
Technical Specifications Polystone® G HG white extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,95 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >22 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1000 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >13 |
| Shore hardness | DIN EN ISO 868 | scale D | >61 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal conductivity | DIN EN ISO 8302 | W / (m * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -50 … 80 |
| Service temperature, short term (max.) | Average | °C | 100 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 67 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,4 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0004 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | >40 |
Technical Specifications Polystone® G HG white pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,95 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >22 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1000 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >13 |
| Shore hardness | DIN EN ISO 868 | scale D | >61 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal conductivity | DIN EN ISO 8302 | W / (m * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -50 … 80 |
| Service temperature, short term (max.) | Average | °C | 100 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 67 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,4 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0004 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | >40 |